TY - JOUR T1 - Comparison of Mechanical and Microstructural Properties of Fly Ash Geopolymer in Water and Chloride Environment AU - Robert, Sharon AU - Ismail, Idawati AU - Ahmadi, Raudhah AU - Abdul Samat, Nur Amalina Shairah JF - Defect and Diffusion Forum VL - 411 SP - 143 EP - 155 SN - 1662-9507 PY - 2021 PB - Trans Tech Publications Ltd DO - 10.4028/www.scientific.net/DDF.411.143 UR - https://www.scientific.net/DDF.411.143 KW - Chloride KW - Curing Regime KW - Durability KW - Fly Ash Geopolymer AB - In cement industry, the emissions of greenhouse gases specifically CO2 from the clinker production led to the need of alternative binders. Geopolymer binder whose precursors are sourced from industrial by-products such as fly ash that are rich is silica and alumina has been studied extensively in the past decades. Chloride attack is one of the threats to concrete structures. Analysis at microstructural level needs to be studied carefully before this binder can be used with confidence. This study attempts to compare the properties of fly ash geopolymer binder when exposed in water and chloride solution. Fly ash geopolymer pastes were prepared using 12M sodium hydroxide (NaOH) as activator. The pastes were tested under two separate curing conditions, i.e in ambient and in distilled water. Compressive strength test along with microstructure properties of samples cured at 7, 14 and 28 days were conducted via Universal testing machine, Fourier Transform Infra-Red (FTIR) spectroscopy and Scanning Electron Microscope with Energy-dispersive X-ray (SEM-EDX). After 28 days of curing, these samples were immersed in 10% sodium chloride (NaCl) solution for another 56 days. Samples cured in ambient condition showed better mechanical performance than those in distilled water. Their differences in compressive strength were also seen consistent with the FTIR results. Samples exposed to NaCl and distilled water showed similar mechanical performance and microstructural properties. Based on SEM-EDX analysis, samples cured in ambient were rich in silica and alumina while the intensity of these compounds were observed to reduce when exposed to distilled water. Samples cured in ambient showed stronger intensity of Si/Al gel as compared to samples exposed to chloride environment and distilled water and these were consistent with the compressive strength results obtained. When immersed in water, concentration gradient changes in the liquid phases, leading to ions diffusion and causing decrement in strength and durability of the solids in fly ash geopolymer. ER -